Anisotropic mechanical properties of nickel foams fabricated by powder metallurgy


Yamada, Yasuo; Banno, Takumi; Li, Yuncang; Wen, Cui'e


In the present study, porous nickel foam samples with pore sizes of 20 μm and 150 μm and porosities of 60 % and 70 % were fabricated by the space-holding sintering method via powder metallurgy. Electron scanning microscopy (SEM) and Image-Pro Plus were used to characterise the morphological features of the porous nickel foam samples. The anisotropic mechanical properties of porous nickel foams were investigated by compressive testing loading in different directions, i.e. the major pore axis and minor pore axis. Results indicated that the nominal stress of the nickel foam samples increases with the decreasing of the porosity. Moreover, the foam sample exhibited significantly higher nominal stress for loading in the direction of the major pore axis than loading in direction of the minor pore axis. It is also noticeable that the nominal stress of the nickel foams increases with the decreasing of the pore size. It seems that the deformation behaviour of the foams with a pore size in the micron-order differs from those with a macro-porous structure.

Publication year


Publication type

Conference paper


Materials Science Forum: Eco-Materials Processing and Design IX: selected papers from the 9th International Symposium on Eco-Materials Processing and Design, Changwon, Korea, 07-09 January 2008 / Byungsei Jun, Hyungsun Kim, Chanwon Lee and Soo Wohn Lee (eds.), Vol. 569, pp. 277-280


Trans Tech Publications




Copyright © 2008 Trans Tech Publications.